Composite Materials Selector Guide
117-1
Flame retardant high toughness system.
Meets
FAR 25.853
NASA Out-gassing
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
250 – 300120 – 150
301
Industry standard for 30 years. Toughened system with controlled flow.
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
250 – 300120 – 150
301T
Derived from 301 with optimized semi-transparent aesthetics.
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
250 – 300120 – 150
304-1
Highly toughened system with good impact resistance.
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
250 – 300120 – 150
307
Specifically designed for thick structures with low exotherm.
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
Less than 250Less than 120
316
Flame retardant system designed for electrical applications.
Meets
UL 94 V-0
Cure Temp
250 – 320120 – 160
Service Temp
18082
Tg
Less than 250Less than 120
350
General purpose high temperature cure system.
Cure Temp
Greater than 320120 – 160
Service Temp
270132
Tg
Greater than 300Greater than 150
321
High Tg with B-basis allowables.
Meets
AGATE B-Basis Allowables
Cure Temp
250 – 320120 – 160
Service Temp
250121
Tg
250 – 300120 – 150
4030
FST system with low heat release properties.
Meets
FAR 25.853
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
250 – 300120 – 150
4550
Toughened bismaleimide (BMI) system, cost-competitive solution for a high Tg.
Cure Temp
Greater than 320Greater than 160
Service Temp
400205
Tg
Greater than 300Greater than 150
4565HT
Toughened bismaleimide (BMI) system with our highest Tg to date.
Cure Temp
Greater than 320Greater than 160
Service Temp
450230
Tg
Greater than 300Greater than 150
4708
OOA processable, highly toughened system with NCAMP data.
Meets
NCAMP Database
Cure Temp
250 – 320120 – 160
Service Temp
250121
Tg
250 – 300120 – 150
5300-1
Low temperature variable cure system with long out-time.
Cure Temp
Less than 250Less than 120
Service Temp
20093
Tg
250 – 300120 – 150
6600
OOA processable, highly toughened high temperature cure system.
Meets
DMS 2224 (not qualified to QPL)
Cure Temp
Greater than 320Greater than 160
Service Temp
350177
Tg
Greater than 300Greater than 150
1101
General purpose sandwich and laminating adhesive prepreg.
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
Less than 250Less than 120
1102
Long out-time adhesive prepreg.
Cure Temp
250 – 320120 – 160
Service Temp
18082
Tg
Less than 250Less than 120
1106
Flame retardent sandwich and laminating adhesive prepreg.
Meets
FAR 25.853
Cure Temp
250 – 320120 – 160
Service Temp
18082
Tg
Less than 250Less than 120
101
General purpose adhesive.
Meets
MIL-A-25463
MMM-A-132
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
Less than 250Less than 120
102
Long out-time adhesive.
Cure Temp
250 – 320120 – 160
Service Temp
18082
Tg
Less than 250Less than 120
106
Flame retardant adhesive.
Meets
FAR 25.853
MIL-A-25463
MMM-A-132
Cure Temp
250 – 320120 – 160
Service Temp
18082
Tg
Less than 250Less than 120
3500
High peel and shear strength adhesive.
Meets
MIL-A-25463
MMM-A-132
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
250 – 300120 – 150
5300-1A
Low temperature variable cure adhesive with long out-time.
Cure Temp
Less than 250Less than 120
Service Temp
20093
Tg
Less than 250Less than 120
HMT301
Toughened towpreg, controlled flow with versatile processing.
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
250 – 300120 – 150
HMT316
Flame retardant towpreg designed for electrical applications
Meets
UL 94 V-0
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
250 – 300120 – 150
HMT317
General purpose towpreg.
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
250 – 300120 – 150
HMT321
High Tg towpreg.
Cure Temp
250 – 320120 – 160
Service Temp
250121
Tg
250 – 300120 – 150
HMT321FR
High Tg towpreg with flame retardency.
Meets
FAR 25.853
Cure Temp
250 – 320120 – 160
Service Temp
250121
Tg
250 – 300120 – 150
HMT4030
FST towpreg with low heat release properties.
Meets
FAR 25.853
Cure Temp
250 – 320120 – 160
Service Temp
20093
Tg
250 – 300120 – 150
HMT507
Towpreg designed for pressure vessels. Cures at 205°F, in polyethylene’s limits.
Cure Temp
250 – 320120 – 160
Service Temp
220105
Tg
250 – 300120 – 150
HMT5300
Low temperature variable cure towpreg with long out-time.
Cure Temp
Less than 250Less than 120
Service Temp
20093
Tg
250 – 300120 – 150
HMT6600
Highly toughened, high temperature cure towpreg.
Cure Temp
Greater than 320Greater than 160
Service Temp
350176
Tg
Greater than 300Greater than 150
51-301
Syntactic expanding core splice adhesive with a 2:1 to 3:1 expansion ratio.
Cure Temp
250 – 320120 – 160
Service Temp
18082