Divinycell F

diab

Divinycell F


MANUFACTURER

DIAB


Description

Divinycell H has been widely used over many years in virtually every application area where sandwich composites areemployed including the marine (leisure, military and commercial), land transportation, wind energy, civil engineering/infrastructure and general industrial markets.


Properties
Property Method Unit H35 H45 H60 H80 H100 H130 H160 H200 H250
Compressive Strength2
ASTM D 1621
MPa
0.45
0.6
0.9
1.4
2.0
3.0
3.4
5.4
7.2
psi
65
87
130
203
290
435
493
783
1,044
Compressive Modulus2
ASTM D 1621
MPa
40
50
70
90
135
170
200
310
400
psi
5,800
7,250
10,150
13,050
19,575
24,650
29,000
44,965
58,015
Tensile Strength2
ASTM D 1623
MPa
1.0
1.4
1.8
2.5
3.5
4.8
5.4
7.1
9.2
psi
145
203
261
363
508
696
783
1,030
1,334
Tensile Modulus2
ASTM D 1623
MPa
49
55
75
95
130
175
205
250
320
psi
7,105
7,975
10,875
13,775
18,850
25,375
29,730
36,250
46,400
Shear Strength
ASTM C 273
MPa
0.4
0.56
0.76
1.15
1.6
2.2
2.6
3.5
4.5
psi
58
81
110
167
232
319
377
508
653
Shear Modulus
ASTM C 273
MPa
12
15
20
27
35
50

73

73
97
psi
1,740
2,175
2,900
3,915
5,075
7,250
10,590
10,590
14,070
Shear Strain
ASTM C 273
%
9
12
20
30
40
40
40
45
45
Nominal Density1
ISO 845
kg/m³
38
48
60
80
100
130
160
200
250
lb/ft³
2.4
3.0
3.8
5.0
6.3
8.1
10.0
12.5
15.6
1. Typical density variation ± 10%
2. Perpendicular to the plane. All values measured at +23°C (73.4°F).
 